Surface modification of polymer nanocomposites by glow discharge plasma treatment

Abstract

Systematic study was carried out to characterize the effects of Argon ion plasma on nanocomposite polymer membrane. Nanoparticles of cobalt (Co) are synthesized by chemical root. 20 micron nanocomposite polymeric membranes were prepared using solution casting and spin coating method. Argon ion plasma treatment was done for these membranes. These membranes were characterized before and after plasma treatment to make comparative study by different technique such as optical microscopy, SEM-scanning electron microscope, Fourier transform infrared spectroscopy. Results show that plasma treatment is a quite effective tool for improving surface and chemical properties of composite membranes with unique characteristics.Досліджено вплив іонно-плазмової обробки на властивості мембрани з нанокомпозитного полімеру. Наночастинки кобальту одержано хімічним синтезом. Мембрани завтовшки 20 mm виготовлено нанесенням нанокомпозитного полімеру з розчину з подальшою іонно-плазмовою обробкою. Мембрани вивчено перед та після їх обробки плазмою методами оптичної мікроскопії, сканівної електронної мікроскопії та інфрачервоної Фур’є-спектроскопії. Виявлено, що іонно-плазмова обробка – ефективний засіб поліпшення поверхневих та хімічних властивостей мембран з нанокомпозитних матеріалів.Исследовано влияние ионно-плазменной обработки на свойства мембраны из нанокомпозитного полимера. Наночастицы кобальта получены химическим синтезом. Мембраны толщиной 20 mm изготовлены нанесением нанокомпозитного полимера с раствора с последующей ионно-плазменной обработкой. Мембраны изучены до и после обработки плазмой методами оптической микроскопии, сканирующей электронной микроскопии и инфракрасной Фурье-спектроскопии. Выявлено, что ионно-плазменная обработка – эффективное средство улучшения поверхностных и химических свойств мембран с нанокомпозитных материалов.