Investigation of electric arc discharge plasma between one-component Cu and Ni and composite Ag-Ni electrodes

Abstract

Plasma of electric arc between one-component Cu and Ni and composite Ag-Ni electrodes was studied by means of optical emission spectroscopy. Radial temperature profiles of plasma column were obtained using Boltzmann plot techniques at arc currents of 3.5 and 30 A. Radial distributions of plasma electron density of electric arc discharge between Cu and Ni and Ag-Ni electrodes were measured as well at currents 3.5 and 30 A. Equilibrium of plasma composition was calculated. The properties of material erosion processes on the electrodes’ surface are studied.

Методами оптической спектроскопии исследована плазма электродугового разряда между однокомпонентными Cu и Ni и композитными Ag-Ni-электродами. С помощью диаграмм Больцмана получены радиальные распределения плазменного столба для дуги током 3,5 и 30 А. Проведены измерения радиальных распределений электронной концентрации плазмы дугового разряда током 3,5 и 30 А между Cu и Ni и Ag-Ni-электродами. Рассчитан равновесный состав плазмы. Исследованы свойства эрозионных процессов материала на поверхности электродов.

Методами оптичної емісійної спектроскопії досліджена плазма електродугового розряду між однокомпонентними Cu та Ni і композитними Ag-Ni електродами. Радіальні розподіли температури плазмового стовпа отримані з діаграм Больцмана для дуги струмом 3,5 та 30 А. Виміряні радіальні розподіли електронної концентрації плазми дугового розряду струмом 3,5 та 30 А між Cu та Ni and Ag-Ni-електродами. Розрахований рівноважний склад плазми. Досліджені властивості ерозійних процесів матеріалу на поверхні електродів.