The relaxation of magnetomechanical effect in silicon crystals under cyclic magnetic treatment

Abstract

The experimental magnetic treatment conditions of silicon crystals in a weak (B = 0.17 T) magnetic field which provide a long-term stability of magnetomechanical effect (MME) have been investigated. It is established that at long-term and cyclic magnetic processing, the MME relaxation is slowed down. The correlation character between the magnetic processing duration of investigated samples and MME relaxation time is established to be linear. A possible reason of MME prolongation at long-term and cyclic magnetic processing is absorption processes and interdefect reactions on the magneticfield- activated silicon surface.

Досліджено експериментальні режими магнітної обробки кристалів кремнію у слабкому (В = 0,17 Тл) магнітному полі, які забезпечують тривалу стабільність магнітомеханічного ефекту (ММЕ). Виявлено, що при тривалій та циклічній магнітній обробці релаксація ММЕ сповільнюється. Встановлено лінійний характер зв'язку між часом магнітної обробки, що досліджуються, зразків і часом релаксації ММЕ. Імовірною причиною пролонгації ММЕ при тривалій і циклічній магнітній обробці є адсорбційні процеси та міждефектні реакції на магнітоактивованій поверхні кремнію.

Исследованы экспериментальные режимы магнитной обработки кристаллов кремния в слабом (В = 0,17 Тл) магнитном поле, которые обеспечивают длительную стабильность магнитомеханического эффекта (ММЭ). Обнаружено, что при длительной и циклической магнитной обработке релаксация ММЭ замедляется. Установлен линейный характер связи между временем магнитной обработки исследуемых образцов и временем релаксации ММЭ. Вероятной причиной пролонгации ММЭ при длительной и циклической магнитной обработке являются адсорбционные процессы и междефектные реакции на магнитоактивированной поверхности кремния.