Determination of tribological and mechanical properties of SnPbCuSb (white metal) bearings

Abstract

White metals (SnPbCuSb) are widely used as journal bearing materials for tin and lead based alloys. In this study, tribological and mechanical properties of these journal bearings manufactured from Sn based SnPbCuSb, pure Sn, pure Pb bearings and from alloy elements, pure Cu metals were determined. SAE 1050 steel shaft (journal) was used as a counter abrader. Wear experiments were carried out in every 30 min for the total of 150 min by using radial journal bearing wear test rig. It was shown that the lowest friction coefficient of bearing and journal wear loss occurred in SnPbCuSb alloyed bearing.

Исследовано трибологические и механические свойства материала SnPbCuSb, который используют для производства подшипников скольжения. Стержень подшипников изготовлен из стали SAE 1050 и использован как показатель (датчик) износа. Испытывали на износ каждые 30 min в течение 150 min, используя радиальную машину с подшипником. Наиболее низкий коэффициент трения и наибольшие потери от трения в подшипника из легированного сплава SnPbCuSb.

Досліджено трибологічні та механічні властивості матеріалу SnPbCuSb, який використовують для виробництва підшипників ковзання. Стрижень підшипників виготовлено зі сталі SAE 1050 і використано як показник (давач) зносу. Випробовували

Fig. 8. SEM microstructure of tensile fracture surface of SnPbCuSb bearing material. ×500. кожні 30 min впродовж 150 min, застосовуючи радіальну машину з підшипником. Найнижчий коефіцієнт тертя опорного підшипника та найбільші втрати від тертя у підшипника з легованого сплаву SnPbCuSb.